S-Glass IFayibha amandla aphezulu
S-Glass IFayibha amandla aphezulu
Iintsinga zeglasi zamandla aphezulu ezenziwe kwi-magnesium alumino silicate inkqubo yeglasi ehlangabezana neemfuno zesicelo somkhosi ziye zaphuhliswa kwaye zafakwa kwimveliso yevolumu ukusukela kwi-70's & 90's kwinkulungwane yokugqibela ngokulandelelanayo.
Xa kuthelekiswa ne-E Glass fiber, babonisa i-30-40% yamandla aphezulu aphezulu, i-16-20% imodulus ephezulu yokuqina. ikhefu, ukuguga okuphezulu kunye nokumelana nomhlwa, iipropathi ezikhawulezayo zokukhupha intlaka.
| Uphawu | |
| ●Ukomelela kakuhle. ● Imodyuli ephezulu yokunwebeka ● 100 ukuya kwi-150 degrees celsius ukunyamezela ubushushu obungcono ● I-10 iphinda iphinde ixhathise ukukhathala ●Ukumelana nempembelelo egqwesileyo ngenxa yobude obuphezulu bokwaphuka ● Ukuguga okuphezulu kunye nokuxhathisa umhlwa ● Iimpawu zokukhupha intlaka ngokukhawuleza ● Ukonga ubunzima kwintsebenzo efanayo |  |
Isicelo
Imizi-mveliso ye-aerospace, yaselwandle neyeengalo ngenxa yokuqina kwayo okuphezulu kunye nemodyuli ephezulu yokunwebeka xa ithelekiswa ne-e-glass.
Iphepha lomhla le-S-Glass kunye ne-E-glass
| Icwecwe leDatha le-S-Glass kunye ne-E-Glass | ||
|
|
| |
| Iipropati | S-iglasi | I-E-Glass |
| Amandla eFayibha eNgcono enyulu (Mpa) | 4100 | 3140 |
| Amandla Okuqina (Mpa) ASTM 2343 | 3100-3600 | 1800-2400 |
| I-Tensile Modulus(Gpa) ASTM 2343 | 82-86 | 69-76 |
| Elongation to Break(%) | 4.9 | 4.8 |
Iipropati
| Iipropati | BH-HS2 | BH-HS4 | Iglasi ye-E |
| Amandla e-virgin fiber tensile (Mpa) | 4100 | 4600 | 3140 |
| Amandla e-Tensi1e(MPA) ASTM2343 | 3100-3600 | 3300-4000 | 1800-2400 |
| I-Tensile Modulus (GPa)ASTM2343 | 82-86 | 83-90 | 69-76 |
| Elongation to break(%) | 49 | 54 | 48 |